​Product Introduction
UNS N06030 is a nickel-based alloy with a high chromium content of about 37% nickel, which provides better corrosion resistance than most other nickel-based and iron-based alloys to commercial phosphoric acid [TJC STEEL]and the mixed environments of many highly oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid. N06030 can prevent the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.
 
 
Chemical Composition (%):
Ni:Rest;
Cr: 28-31.5;
C: 0.03 Max;
Fe:13-17;
Mo:4-6;
W: 1.5 4;
Cu: 1-2.4;[TJC STEEL]
Co:5max;
Si: 0.2-0.8;
Mn: 0.3-1.5;
P: 0.04 Max;
S: 0.02 Max;
Nb: 0.3-1.5;
 
 
 
Physical Property
Density: 8.23 g/cm after;
Melting Point:1335-1380℃;
Electrical Resistivity:1.28;
Thermal Conductivity:14;[TJC STEEL]
Specific Heat Capacity:398;
 
 
Mechanical Property
Heat Treatment:Solution&Annealed;
Tensile Strength:586MPa min;
Yield Strength: 241MPa min;[TJC STEEL]
Elasticity Modulus:212 min;
Elongation: 30% min;
 
 
Product Standard
UNS N06030 Bar-ASME SB581; UNS N06030 Plate-ASME SB582; UNS N06030 Seamless Pipe-ASME SB622; UNS N06030 [TJC STEEL]Welded Pipe-ASTM B619,ASTM B626; UNS N06030 Forged Products-ASTM B462,etc.
 
 
Product Characteristics
A. Excellent corrosion resistance in alkaline media;
B. Good corrosion resistance against cavitation;
C. Has good corrosion resistance to diluted [TJC STEEL]inorganic acids (such as sulfuric acid, hydrochloric acid);
 
 
Application Field
A.Chemical process equipment;
B.High temperature heat exchanger;
C.Catalyst carrier;[TJC STEEL]
D.Petrochemical storage tanks;
E.Components of nuclear equipment;

Product Introduction
 
UNS N06002 is a nickel-chromium alloy with the addition of drill and tungsten. The alloy has excellent oxidation resistance[TJC STEEL] at high temperatures up to 1200℃ and can also be used in neutral and reductive atmospheres. At the same time, the alloy can resist carbonization and nitriding atmosphere.
 
 
Chemical Composition (%):
Ni:Rest;
W: 0.2-1.0;
Fe:17-22;
Mn: 1.0 Max;
C: 0.05-0.15;
Si: 1.0 Max;[TJC STEEL]
S: 0.03 Max;
Cr: 20.5-23;
Mo:8-10;
P: 0.04 Max;
Co: 0.5-2.5;
 
 
Physical Property
Density: 8.28 g/cm after;
Melting Point:1260-1355℃;
 
 
 
Mechanical Property[TJC STEEL]
Tensile Strength:690MPa min;
Yield Strength:276MPa min;
Elongation(%):35min;
 
 
Product Standard
N06002 Bar-ASTM B572; N06002 Plate-ASTM B435; N06002 Seamless Pipe-ASTM B622; N06002 Welded Pipe:ASTM B619;[TJC STEEL] N06002 Pipe Fitting-ASTM B626; N06002 Forged Product-ASTM B575,etc.
 
 
 
Product Characteristics
A. Good cold and hot processing performance;
B. With satisfactory welding performance, it can be welded by argon arc welding, seam welding, spot welding and other [TJC STEEL]methods;
C. The adhesion of surface oxides and welding slag around the weld is stronger than that of stainless steel;
 
Application Field
1.Industrial and aerospace turbines;
B.Spiral tubes in petrochemical furnaces;
C.Industrial furnace components (support rolls, grids, ribbons and radiation tubes);
D.High temperature gas cooled nuclear reactors;
E.Industrial and aviation[TJC STEEL] steam turbines
F.Spiral tubes in petrochemical furnaces
G.Industrial furnace components (support rolls, grids, ribbons and radiation tubes)
H.High temperature gas cooling nuclear reactors